Poly(o-methylaniline) (poly-o-toluidine, PTOL) was synthesized by chemical oxidation of o-toluidine with ammonium peroxydisulfate in an aqueous 1.0 mol L-1 HCl solution. The progress of polymerization was followed by measuring the open-circuit potential (OCP) of a Pt electrode immersed in the reaction medium with the polymerization time. The chemical synthesis of PTOL was carried out at different monomer:oxidant (M:O) molar ratios (4:1, 2:1, 1.5:1, 1:1, and 0.66:1), and the products obtained were characterized by infrared spectroscopy, gel permeation chromatography, and X-ray diffraction. The molecular weight and percentage of crystallinity of PTOL are higher for samples synthesized in an excess of the monomer, i.e. at higher M:O ratios. However, the yield of PTOL prepared at higher M:O ratios is considerably low, in particular at a 4:1 M:O ratio, which is the M:O ratio most commonly used in the literature to synthesize polyaniline and its derivatives.

This paper describes a sample holder for the electrical measurement of oxides or conducting polymers in the form of pellets or films which are used as gas sensors. The system makes it possible to control the sample temperature, the gas pressure and composition. The temperature in the sample can be changed from 25ºC to 450ºC, and the gas pressure in the chamber is controlled between 5 ¥ 10-4 and 1000 mbar. The performance of the system in resistance measurements of doped tin oxide pellets and polyaniline films deposited on platinum electrodes for methane is analyzed.